Micro-electro mechanical system (MEMS) structures with through substrate vias and methods of forming the same

ABSTRACT

The present disclosure includes micro-electro mechanical system (MEMS) structures and methods of forming the same. Substrates of the MEMS structures are bonded together by fusion bonding at high processing temperatures, which enables more complete removal of chemical species from the dielectric materials in the substrates prior to sealing cavities of the MEMS structures. Fusion bonding of MEMS structures reduces outgassing of chemical species and is compatible with the cavity formation process. The MEMS structures bonded by fusion bonding are mechanically stronger compared to eutectic bonding due to a higher bonding ratio. In addition, fusion bonding enables the formation of through substrate vias (TSVs) in the MEMS structures.

CROSS-REFERENCE TO RELATED APPLICATION

The present application claims priority of U.S. Provisional PatentApplication No. 61/593,187, filed on Jan. 31, 2012, which isincorporated herein by reference in its entirety.

TECHNICAL FIELD

The present disclosure relates generally to the field of semiconductorpackage systems and, more particularly, to micro-electro mechanicalsystem (MEMS) structures and methods of forming the same.

BACKGROUND OF THE DISCLOSURE

The semiconductor integrated circuit (IC) industry has experienced rapidgrowth. Technological advances in IC materials and design have producedgenerations of ICs where each generation has smaller and more complexcircuits than the previous generation. In the course of IC evolution,functional density (i.e., the number of interconnected devices per chiparea) has generally increased while geometric size (i.e., the smallestcomponent that can be created using a fabrication process) hasdecreased. Such advances have increased the complexity of processing andmanufacturing ICs and, for these advances to be realized, similardevelopments in IC processing and manufacturing are needed.

Micro-electro mechanical system (MEMS) devices are a recent developmentin the field of integrated circuit technology. MEMS devices includedevices fabricated using semiconductor technology to form mechanical andelectrical features. Examples of MEMS devices include gears, levers,valves, and hinges. Common applications of MEMS devices includeaccelerometers, pressure sensors, actuators, mirrors, heaters, andprinter nozzles.

BRIEF DESCRIPTION OF THE DRAWINGS

The present disclosure is best understood from the following detaileddescription when read with the accompanying figures. It is emphasizedthat, in accordance with the standard practice in the industry, variousfeatures are not drawn to scale and are used for illustration purposesonly. In fact, the dimensions of the various features may be arbitrarilyincreased or reduced for clarity of discussion.

FIG. 1 is a schematic cross-sectional view of an exemplary micro-electromechanical system (MEMS) structure, in accordance with some embodiments.

FIGS. 2A-2H are cross-sectional views of a sequential process ofpackaging a MEMS device, in accordance with some embodiments.

DETAILED DESCRIPTION

Generally, a micro-electro mechanical system (MEMS) package system has aplurality of substrates that are bonded to each other. In a MEMS packagesystem, a MEMS device is disposed in at least one cavity that is sealedby the bonded substrates. The cavity is vacuumed such that the operationof the MEMS device in the space is less affected. The substrates mayhave a plurality of dielectric materials that are used to form anintegrated circuit. Chemical species may outgas from the dielectricmaterials into the cavity. The gases may change the environment aroundthe MEMS device and affect the operation of the MEMS device.

It is understood that the following disclosure provides many differentembodiments, or examples, for implementing different features of thedisclosure. Specific examples of components and arrangements aredescribed below to simplify the present disclosure. These are, ofcourse, merely examples and are not intended to be limiting. Inaddition, the present disclosure may repeat reference numerals and/orletters in the various examples. This repetition is for the purpose ofsimplicity and clarity and does not in itself dictate a relationshipbetween the various embodiments and/or configurations discussed.Moreover, the formation of a feature on, connected to, and/or coupled toanother feature in the present disclosure that follows may includeembodiments in which the features are formed in direct contact, and mayalso include embodiments in which additional features may be formedinterposing the features, such that the features may not be in directcontact. In addition, spatially relative terms, for example, “lower,”“upper,” “horizontal,” “vertical,” “above,” “below,” “up,” “down,”“top,” “bottom,” etc. as well as derivatives thereof (e.g.,“horizontally,” “downwardly,” “upwardly,” etc.) are used for ease of thepresent disclosure of one feature's relationship to another feature. Thespatially relative terms are intended to cover different orientations ofthe device including the features.

The present disclosure is associated with MEMS structures and methods offorming the same. The substrates of the MEMS structures are bondedtogether by fusion bonding at relatively high processing temperatures,which enables more complete removal of chemical species from thedielectric materials in the substrates prior to sealing cavities of theMEMS structures. Fusion bonding makes high temperature annealing on bothsides wafers possible, which reduces outgassing of chemical speciesduring the cavity formation process. The MEMS structures bonded byfusion bonding are mechanically stronger compared to metal bonding dueto a higher bonding ratio. In addition, fusion bonding enables theformation of through substrate vias (TSVs) in the MEMS structureswithout degrading yield. Following are descriptions regarding variousexemplary MEMS structures and methods of forming the same. It is notedthat the MEMS structures and methods described below are merelyexemplary. The scope of this application is not limited thereto.

FIG. 1 is a schematic cross-sectional view of an exemplary micro-electromechanical system (MEMS) structure 100 in accordance with someembodiments. In FIG. 1, a substrate structure 130 is bonded to asubstrate structure 105. In some embodiments, the substrate structure105 includes substrate structures 110 and 120 that are bonded to eachother. In some embodiments, the substrate structures 105 and 130 areassembled to form a hermetic or non-hermetic package system. In someembodiments, the substrate structures 110, 120 and 130 includesubstrates 112, 122 and 132, respectively. In some embodiments, thesubstrate structure 130 is referred to as a capping substrate structure.The substrate 132 is referred to as a capping substrate. The substrate122 is referred to as a MEMS substrate. The substrate 112 is referred toas an integrated circuit substrate. However, substrate 132 may haveintegrated circuits and substrate 112 may not include any integratedcircuits in some embodiments.

In some embodiments, the substrates 112, 122 and 132 each include thesame or different materials and may comprise any suitable combination ofmaterials. For example, the substrates 112, 122 and 132 each can be asemiconductor substrate that includes an elementary semiconductorincluding silicon and/or germanium; a compound semiconductor includingsilicon carbide, gallium arsenide, gallium phosphide, indium phosphide,indium arsenide, and/or indium antimonide; an alloy semiconductorincluding SiGe, GaAsP, AlInAs, AlGaAs, GaInAs, GaInP, and/or GaInAsP; orcombinations thereof. The alloy semiconductor substrate can have agradient SiGe feature in which the Si and Ge composition change from oneratio at one location to another ratio at another location of thegradient SiGe feature. The alloy SiGe can be formed over a siliconsubstrate. The SiGe substrate may be strained. Furthermore, thesubstrates 112, 122 and/or 132 can be a semiconductor on insulator(SOI). In some examples, the substrates 112, 122 and/or 132 include adoped epi layer. In other examples, the substrates 112, 122 and/or 132include a multilayer compound semiconductor structure. Alternatively,the substrates 112, 122 and/or 132 include a non-semiconductor material,such as a glass, fused quartz, or calcium fluoride.

In some embodiments, the substrate structures 110, 120 and/or 130include at least one complementary metal-oxide-semiconductor (CMOS)integrated circuit, at least one micro-electro mechanical system (MEMS)device, other integrated circuits, and/or any combinations thereof. Insome embodiments, the substrate structures 110, 120 and/or 130 includean interposer structure, which represents a substrate that may merelyinclude a conductive wire routing for an electrical connection and befree from including any active device.

For example, the substrate structure 105 includes an integrated circuitstructure 111 formed over the substrate 112 as shown in FIG. 1. In someembodiments, the integrated circuit structure 111 is formed, forexample, by a complementary metal-oxide-semiconductor (CMOS) technology.The integrated circuit structure 111 includes, for example but notlimited to, a logic circuit, an analog circuit, a mixed-signal circuit,and/or any suitable integrated circuit. In some embodiments, theintegrated circuit structure 111 includes an interconnect metallizationstructure (not labeled) that is formed over the substrate 112. Theinterconnect metallization structure is configured to provide electricalinterconnections among active devices and/or passive devices formed onand/or over the substrate 112 and/or 122.

In some embodiments, the interconnect metallization structure includesinter-metal dielectric (IMD) materials. In some embodiments, each of theIMD materials include at least one material, such as silicon oxide,silicon nitride, silicon oxynitride, silicon carbide, siliconoxycarbide, low dielectric constant (low-k) dielectric material, ultralow-k dielectric material, other dielectric materials, or anycombinations thereof. In some embodiments, the substrate structures 110and 120 are bonded together by any suitable method, such as fusion oreutectic bonding processes. For example, the fusion bonding processinvolves bringing the substrate structures 110 and 120 into intimatecontact, which causes the substrates 110 and 120 to bond together due toatomic attraction forces (i.e., Van der Waals forces). The substratestructures 110 and 120 are then subjected to an annealing process, afterwhich a solid bond, e.g., a covalent bond, may be formed between thesubstrate structures 110 and 120. A temperature for the annealingprocess is any suitable temperature, such as between about 200° C. andabout 350° C. The fusion bonding process can arise from SiO₂/Si bonding,Si/Si bonding, and/or other suitable bonding.

In some embodiments, the eutectic bonding process is applied between anyalloy suitable for the bonding temperature boundary condition. Forexample, the eutectic bonding process includes metal/metal bondingand/or metal/semiconductor bonding, such as Ge/Al bonding, Ge/Aubonding, Si/Au bonding, Si/Al bonding, and/or other suitable bonding. Ifthe bonding process involves a substrate including CMOS devices, thebonding temperature is controlled to be near or lower than a CMOS devicetemperature. The eutectic bonding processes may occur at high pressureand at any suitable temperature, such as between about 400° C. and 450°C.

In some embodiments, the interconnect metallization structure includes aplurality of metallic layers (not shown). The metallic layers areelectrically coupled with each other through at least one via plugstructure, e.g., a via plug structure. In some embodiments, theinterconnect metallization structure is made of at least one material,such as aluminum (Al), copper (Cu), tungsten (W), cobalt (Co), platinum(Pt), silicon (Si), germanium (Ge), titanium (Ti), tantalum (Ta), gold(Au), nickel (Ni), tin (Sn), other suitable metallic materials, and/orany combinations thereof. Alternatively, the interconnect metallizationstructure includes doped polysilicon, which can sustain higherprocessing temperature than some metal materials.

Referring again to FIG. 1, the substrate structure 120 includes at leastone MEMS device, e.g., a MEMS device 124. In some embodiments, the MEMSdevice 124 includes a plurality of elements formed of metal,polysilicon, dielectric, and/or other materials. The MEMS device 124 caninclude materials typically used in a CMOS fabrication process. Anyconfiguration of the MEMS device 124 is possible, depending on thedesired functionality. One or more of the elements depicted may bedesigned to provide MEMS mechanical structures. The MEMS mechanicalstructures may include structures or elements operable for mechanicalmovement. The MEMS device 124 can be formed using processes used in CMOSfabrication, for example, photolithography, etching processes (e.g., wetetch, dry etch, plasma etch), deposition processes, plating processes,and/or other suitable processes, which may utilize one or more maskingor patterning steps. In some embodiments, the MEMS device 124 includes amotion sensor (e.g., a gyroscope, an accelerometer, etc.), a radiofrequency (RF) MEMS device (e.g., an RF switch, filter, etc.), anoscillator, a MEMS microphone, micro mirror or any other MEMSstructures.

FIG. 1 shows that the substrate structures 105 and 130 are bondedtogether by bonding structure 117 on substrate structure 105, or onsubstrate 122, and bonding pad structure 134 on substrate structure 130,in accordance with some embodiments. The bonding pad structures 117 and134 each include a bonding material that is suitable for bonding. Forexample, the bonding pad structure 134 includes at least onesemiconductor material, e.g., Ge, Si, silicon-germanium(Si_(x)Ge_(1-x)), other semiconductor materials, and/or any combinationsthereof. The bonding pad structure 117 includes at least one metallicmaterial, e.g., Al, Cu, Ti, Ta, Au, Ni, Sn, other metallic materials,and/or any combinations. In other embodiments, the bonding padstructures 117 and 134 each include at least one metallic material,e.g., Al, Cu, Ti, Ta, Au, Ni, Sn, other metallic materials, and/or anycombinations.

Bonding pad structures 117 and 134 are bonded together by a thermalprocess to form a eutectic phase after being pressed together. Forexample, if bonding pad structures 134 are made of Ge and bonding padstructures 117 are made of Al, an annealing process at a temperatureranging from about 400° C. to 450° C. would allow bond pad structures117 and 134 be bonded together by eutectic bonding. For bonding of suchbond pad structures, pressure needs to be applied on substratestructures 105 and 130 to hold the bonding pad structures 117 and 134together during the annealing process. Due to the pressure required tohold the bonding pad structures 117 and 134 together, the percentage ofsurfaces occupied by the boding pad structures to the surface area ofsubstrate structures 130 (or 105) having such bond pad structures islimited to increase the pressure applied. In some embodiments, thepercentage of areas of the bonding pad structures, which is also calleda bonding ratio, is limited to about 5%-30% of the area of substratestructures 105 and 130. The bonding ratio reduces the flexibility ofcircuit design, since there are only limited areas available for formingstructures between MEMS devices in the bonded substrates for externalconnection.

In some embodiments, the substrate structure 110 includes a cavity 125,which is below and encircles MEMS device 124 to provide space betweenthe MEMS device 124 and the substrate structure 110. In someembodiments, substrate structure 130 also includes a cavity 135, whichis above and encircles MEMS device 124 to provide space between the MEMSdevice 124 and substrate structure 130. Cavities 125 and 135 allow theMEMS device 124 to move freely. The cavities 125 and 135, or the spacesurrounding the MEMS device 124, are vacuumed such that the operation ofthe MEMS device 124 in the space surrounding it is less affected.Cavities 125 and/or 135 may be formed by a wet or dry etching process,or a combination thereof in accordance with some embodiments. In someembodiments, an HF solution is used in removing dielectric materials,such as silicon dioxide. Using HF solution to remove dielectricmaterial(s) may also be called HF release. The formation of MEMS device124 requires HF release, in accordance with some embodiments. The HFsolution used may attack (or corrode) eutectic bonding structure thatincludes metal. Therefore, it is a challenge to integrate eutecticbonding with MEMS structures.

As shown in FIG. 1, a portion of cavity 125 is formed in the ICstructure 111, which includes one or more IMD materials, as describedabove. Similarly, the cavity 135 of substrate structure 130 may also beformed by removing one or more dielectric layers, which are similar tothe IMD materials in IC structure 111, in the substrate structure 130.The unstable chemicals in the IMD materials, such as unbound chemicalsand/or unstable organic materials could outgas under vacuum pressure,which is what the cavities 125 and 135 are under after bonding. Theoutgassed chemicals could deposit on the MEMS device 124 and/or walls ofthe cavities 125 and 135 to cause performance degradation of the MEMSdevice 124. During the bonding process, the thermal process for formingeutectic bonding of bonding pad structures 134 and 117 could releasepart of the unstable chemicals from the IMD materials. However, therelatively low thermal anneal (or bonding) temperature, such as equal toor less than about 450° C., is insufficient to remove (or release) allunstable chemicals in the IMD materials. The unstable chemicals left inthe IMD materials could outgas after bonding when the MEMS device 124 isunder vacuum pressure to degrade performance. In FIG. 1, H₁ defines thethickness of substrate 132.

After eutectic bonding is performed, external contacts are formed, whichinvolves applying mechanical force on the package, on substratestructure 130 or substrate 112. For example, drilling to form openingsin substrate structure 130 or substrate 112 and thinning down substrate112 may be involved. Due to the low bonding ratio, the MEMS package isfragile for such a formation process of external contacts and yieldcould suffer. Therefore, integrating eutectic bonding with the formationprocess of external contacts is challenging.

FIGS. 2A-2H are cross-sectional views of a sequential process ofpackaging a MEMS structure 200, in accordance with some embodiments.FIG. 2A shows a substrate structure 130 is provided and is bonded withsubstrate structure 105. Brief descriptions of substrate structures 130and 105 have been provided above. FIG. 2A shows that the substratestructures 105 and 130 are bonded together by a bonding layer 116through fusion bonding, in accordance with some embodiments. The fusionbonding may be between Si (silicon) and Si or between Si and silicondioxide (SiO₂), in accordance with some embodiments. For example, if thefusion bonding is between Si and Si, a bonding layer 116 made of Si maybe formed on substrate 122 to bond with a Si surface 133 of substrate132, in accordance with some embodiments. In some other embodiments, thebonding layer 116 is formed on substrate 132 to bond with a Si surface123 of substrate 122. In yet some other embodiments, a Si sub-layer 116′is formed on substrate 132 to bond with a Si sub-layer 116″ formed onsubstrate 122 to form layer 116. If the fusion bonding is between Si andSiO₂, the bonding layer 116 is made of SiO₂ and may be formed onsubstrate 132 or substrate 122 to form fusion bonding with a Si surfaceon the other substrate. In some embodiments, the bonding layer hasthickness in a range from about 10 Å to about 2000 Å.

Fusion bonding between Si and Si may be achieved by making the Sisurfaces hydrophobic first. The Si surfaces of the two substrates arethen pressed together and annealed to form Van der Waals bonds betweenSi surfaces on two substrates. If none of the substrates haveinterconnect structures involving metal materials, the substrates may beheated to a high temperature in a range from about 900° C. to about1200° C. during fusion bonding process. The high bonding temperatureenables most of the chemicals in the IMDs to outgas. As a result, theproblem of outgassing described above is reduced in comparison witheutectic bonding. If fusion bonding is between Si and SiO₂, the surfacesof Si and SiO₂ are made hydrophilic first. The Si and SiO₂ surfaces ofthe two substrates are then pressed together and annealed at atemperature in a range from about 500° C. to about 1200° C. to form Vander Waals bonds between Si surfaces on two substrates. A fusion bondingtemperature of about 500° C. is slightly higher than the eutecticbonding temperature of between about 400° C. to about 450° C. Outgassingof IMDs is more complete when the annealing temperature is equal to orgreater than about 450° C. The outgassing of chemicals in the IMDs underSi/SiO₂ fusion bonding at a temperature greater than about 450° C. andless than about 1200° C. would be more complete in comparison toeutectic bonding. Therefore, the outgassing issue is reduced by fusionbonding at the temperature ranges mentioned above. Fusion bonding underthe temperature ranges mentioned above is not compatible with bondingsubstrate structures including a metal interconnect. In the situationthat interconnect is needed, doped polysilicon may be used in place ofmetal materials.

Since fusion bonding does not involve metal, it is compatible with theHF release process used in the formation of MEMS structures. Inaddition, fusion bonding includes surface treatment and high bondingtemperature and does not use pressure as high as the pressure used ineutectic bonding, to push the substrates together. As a result, thebonding ratio for fusion bond is higher, such as in a range from about40% to about 95%, than the bonding ratio of eutectic bonding. In someembodiments, the fusion bonding ratio is in a range from about 50% toabout 95%. Higher bonding ratio of fusion bonding makes the packagedMEMS structures mechanically stronger in comparison with packed MEMSstructures formed using eutectic bonding. Higher bonding ratio of fusionbonding also increases design flexibility by providing a higher numberof locations to place electrical connections in comparison with packedMEMS structures formed using eutectic bonding.

In comparison to eutectic bonding, fusion bonding of substrates to formMEMS package described above reduces outgassing and metal corrosionissues described above. Fusion bonding also makes the packaged MEMSpackage stronger and enables more design flexibility. The concern offragile package by eutectic bonding being incompatible with theformation process of external contacts can be decreased. FIGS. 2B-2H arecross-sectional views of a sequential process of forming externalcontacts utilizing TSVs, in accordance with some embodiments.

FIG. 2B is a cross-sectional view of MEMS structure 200 after a backsideof substrate 132 has been thinned, in accordance with some embodiments.The backside of substrate 132 is thinned to make the TSVs having shorterheights to avoid the aspect ratios of the TSVs being too high. FIG. 2Bshows that substrate 132 is thinned from an original thickness H₁ to athickness H₂. The thinning process can be an etching process, apolishing process, or a grinding process.

After substrate 132 is thinned, the backside surface of substrate 132 ispatterned by a photoresist 141 to expose surface areas for forming TSVs,as depicted in FIG. 2C in accordance with some embodiments. Afterwardsas in FIG. 2D, TSV openings 145 are formed by etching the materiallayers under TSV openings 145 to contact substrate 122 by etching thematerial under the exposed surface areas. Residual photoresist 141 isremoved and an isolation layer 142 is deposited to cover the exposedsurfaces of substrate 132, in accordance with some embodiments. Exposedsurfaces of substrate 132 are covered by the isolation layer 142including inner walls of TSV openings 145. The isolation layer 142 ismade of a dielectric material, such as oxide, nitride, or a combinationof both. One example of a material for the isolation layer 142 issilicon oxide deposited by plasma enhanced chemical vapor deposition(PECVD) using silane or tetraethylorthosilicate (TEOS) as the siliconsource. In some embodiments, the isolation layer has a thickness rangingfrom about 500 Åto about 15000 Å. The isolation layer 132 can also bedeposited (or grown) by a thermal process, such as a thermally grownoxide, or a thermal CVD oxide. Other types of dielectric materials mayalso be used. In some embodiments, the width W₁ of the TSVs is in arange from about 10 microns (μm) to about 150 μm.

After the isolation layer 142 is deposited, the isolation layer 142 at abottom of the TSV openings 145 is removed to expose a conductive surface146 of substrate 122. FIG. 2D shows the MEMS structure 200 after theisolation layer 142 at the bottom of the TSV openings 145 is removed, inaccordance with some embodiments. The conductive surface 146 is madeconductive by doping the substrate 122 with N-type or P-type dopants toincrease the conductivity of semiconductor material of substrate 122, inaccordance with some embodiments. In some embodiments, substrate 122 isprovided as a highly doped substrate. Other mechanisms for forming theconductive surface 146 may also be used. The conductive surface 146enables the TSVs formed to establish ohmic contacts with the conductivesurface 146. Substrate 122 may be doped to enable electrical connectionsbetween the TSVs, the MEMS devices 124 in substrate structure 120, andthe interconnect and devices in substrate structure 110. Alternatively,an interconnect may also be formed to enable the electrical connections.

After the isolation layer 142 at the bottom of TSV openings 145 isremoved to expose conductive surface 146, a contact metal layer 143 isdeposited. The contact metal layer 143 electrically contacts surface146. In some embodiments, the contact metal layer includes at least twosub-layers, a barrier layer and a copper seed layer. The barrier layerestablishes ohmic contact with surface 146 and may be made of one ormore copper barrier materials, such as Ta, TaN, Ti, TiN, CoW, or thelike. The barrier layer provides protection against copper diffusinginto the substrates 132 and 122. The barrier layer can be deposited byPVD (physical vapor deposition), chemical vapor deposition (CVD), atomiclayer deposition (ALD), or other suitable methods. After the depositionof the barrier layer, a copper seed layer is deposited. The similarly,the copper seed layer can be deposited by PVD (physical vapordeposition), chemical vapor deposition (CVD), atomic layer deposition(ALD), or other suitable methods. In some embodiments, thebarrier/Cu-seed layer 143 is made of TaN/Ta barrier and a copper seedlayer. In some embodiments, each thickness of TaN and Ta is betweenabout 100 Å to about 2000 Å, and the thickness of the copper seed isbetween about 1000 Å to about 15000 Å.

After the deposition of the barrier/copper-seed layer 143, MEMSstructure 200 is patterned by a photoresist (not shown) to define areasto receive copper plating. A copper film 144 is than plated on the MEMSstructure 200. The photoresist is then removed. The barrier/Cu-seedlayer 143 not covered by the copper film 144 is then removed after thephotoresist is removed by etching, in accordance with some embodiments.The barrier/copper-seed layer 143 and the copper film 144 form the TSVmetal layer 147. FIG. 2E shows MEMS structure 200 after the excessbarrier/Cu-seed layer 143 is removed, in accordance with someembodiments.

Electrical copper plating (ECP) processes or electroless copper platingprocess used in the metal interconnects of semiconductor devicemanufacturing can be used. In some embodiments, the thickness of thecopper film 144 is less than about 40 mm. In other embodiments, thethickness of the copper film 144 is less than about 30 mm. In yet someother embodiments, the thickness of the copper film 144 is in a rangefrom about 1 mm to about 25 mm. A copper film that is too thick couldresult in substrate warping. In some embodiments, the copper film 144 isdeposited to fill the TSV openings 145 of TSVs 150. In some otherembodiments, the copper film 144 is deposited to partially fill the TSVopenings 145 of TSVs 150, as shown in FIG. 2E. During the formation ofTSVs 150, contact regions 151 next to TSVs 150 are also formed. Contactregions 151 are used to form external contacts, as described below.Details of an exemplary mechanism of forming TSVs can be found in U.S.patent application Ser. No. 12/897,124, titled “Novel SemiconductorPackage With Through Substrate Vias,”and filed on Nov. 4, 2010, which isincorporated herein in its entirety.

FIG. 2F depicts a passivation layer 160 is formed on MEMS structure 200,in accordance with some embodiments. Passivation layer 160 is formed toprotect a surface of MEMS structure 200. In some embodiments, thepassivation layer 160 is made of a polymer, such as an epoxy, polyimide,benzocyclobutene (BCB), polybenzoxazole (PBO), and the like, althoughother soft, often organic, dielectric materials can also be used. Insome embodiments, the passivation layer 160 is a polyimide layer. Insome other embodiments, the passivation layer 160 is a polybenzoxazole(PBO) layer. The passivation layer 160 is soft, and hence has thefunction of reducing inherent stresses on respective substrate. Inaddition, the passivation layer 160 can be formed to a thickness of tensof microns. The passivation layer 160 is then patterned to form openings161 for external contacts, as shown in FIG. 2G in accordance with someembodiments. Openings 161 have a width W₂. In some embodiments, W₂ is ina range from about 50 μm to about 500 μm. A photoresist layer (notshown) is deposited and patterned to define the openings 161 overcontact regions 151.

After openings 161 are formed, an under-bump-metallurgy (UBM) layer 165is formed on the resulted structure of FIG. 2G. In some embodiments, theUBM layer 165 includes a diffusion barrier layer and a seed layer. FIG.2H shows that the UBM layer 165 is formed on the passivation layer 160and lines sidewalls and a bottom of the openings 161, in accordance withsome embodiments. The diffusion barrier layer may be formed of tantalumnitride, although it may also be formed of other materials such astitanium nitride, tantalum, titanium, or the like. The thickness of thediffusion barrier layer is in a range from about 500 Å to about 5000 Å,in some embodiments. In some embodiments, the diffusion barrier layer isformed by physical vapor deposition (PVD) (or sputtering). The seedlayer may be a copper seed layer formed on the diffusion barrier layer.The copper seed layer may be formed of copper or one of copper alloysthat include silver, chromium, nickel, tin, gold, and combinationsthereof. The thickness of the copper seed layer is in a range betweenabout 2000 Å to about 10,000 Å, in some embodiments

In some embodiments, the UBM layer 165 includes a diffusion barrierlayer formed of Ti and a seed layer formed of Cu. In some embodiments,both the diffusion barrier layer, such as a Ti layer, and the seedlayer, such as a Cu layer, are deposited by physical vapor deposition(PVD) (or sputtering) methods. An excess portion of UBM layer 165 notcovering or surrounding openings 161 is removed by patterning andetching. External contacts, such as bumps or wires, may be formed on theUBM layer 165. Details of an exemplary mechanism of forming bumps can befound in U.S. patent application Ser. No. 12/846,353, titled “Mechanismsfor Forming Copper Pillar Bumps,” and filed on Jul. 29, 2010, which isincorporated herein in its entirety. Other mechanisms of forming bumpsor balls as external contacts may also be used.

In one aspect of this description, a device is provided. The deviceincludes a capping substrate, and a substrate structure. The substratestructure includes at least one micro-electro mechanical system (MEMS)device, and the substrate structure is bonded to the capping substrateby a fusion bonding layer. There is at least one cavity surrounding atleast a portion of the MEMS device.

In another aspect of this description, a micro-electro mechanical system(MEMS) structure is provided. The MEMS structure includes a firstsubstrate embedded with a TSV, and the first substrate has a firstcavity. The MEMS structure includes a second substrate structure bondedto the first substrate by a fusion bonding layer, and the secondsubstrate structure including at least one MEMS device. The MEMSstructure includes a third substrate structure coupled to the secondsubstrate structure and the third substrate structure has an integratedcircuit (IC) device. The third substrate structure has a second cavity,and the first and second cavities surround at least a portion of the atleast one MEMS device.

In still another aspect of this description, a method of forming amicro-electro mechanical system (MEMS) structure is provided. The methodincludes providing a first substrate structure and bonding a secondsubstrate structure to the first substrate structure using fusionbonding. The second substrate structure includes at least onemicro-electro mechanical system (MEMS) device, and there is at least onecavity surrounding at least a portion of the MEMS device.

The foregoing outlines features of several embodiments so that thoseskilled in the art may better understand the aspects of the presentdisclosure. Those skilled in the art should appreciate that they mayreadily use the present disclosure as a basis for designing or modifyingother processes and structures for carrying out the same purposes and/orachieving the same advantages of the embodiments introduced herein.Those skilled in the art should also realize that such equivalentconstructions do not depart from the spirit and scope of the presentdisclosure, and that they may make various changes, substitutions, andalterations herein without departing from the spirit and scope of thepresent disclosure.

What is claimed is:
 1. A device comprising: a capping substrate having acavity, wherein the capping substrate has a first surface of silicon;and a substrate structure, wherein the substrate structure includes atleast one micro-electro mechanical system (MEMS) device, wherein theMEMs device is disposed in the cavity, and wherein the substratestructure includes a layer providing a second surface of silicon;wherein the first surface of silicon interfaces the second surface ofsilicon to form a fusion bond interface between the substrate structureand the capping substrate wherein the fusion bond interface is betweenthe silicon of the first surface and silicon of the second surface; atleast one cavity surrounding at least a portion of the MEMS device; atleast one through substrate via (TSV) extending through the cappingsubstrate and the fusion bond interface to contact the substratestructure, wherein the TSV comprises a central region free of conductivematerial and wherein the TSV provides an electrical connection to anintegrated circuit component; and a polymer material in the centralregion of the TSV.
 2. The device of claim 1, wherein the substratestructure includes at least one dielectric layer, wherein the at leastone cavity includes is formed by etching the at least one dielectriclayer.
 3. The device of claim 1, wherein the substrate structureincludes a MEMS substrate having the MEMS device and an integratedcircuit substrate having an integrated circuit.
 4. The device of claim1, wherein the device includes the polymer material over the cappingsubstrate.
 5. The device of claim 1, wherein a bonding layer includingthe fusion bond interface has a thickness in a range from about 10 Å toabout 2000 Å.
 6. The device of claim 1, wherein the TSV has a width in arange from about 10 microns (μm) to about 150 μm.
 7. The device of claim1, wherein a bonding structure is formed over the TSV, and wherein thebonding structure is disposed over and comes in contact with a metallayer used to fill the TSV.
 8. The device of claim 1, wherein the TSVextends through the capping substrate, wherein the interface of thefirst surface of silicon and the second surface of silicon comprises afirst portion and a second portion discontinuous with the first portion,the TSV extending through the first portion of the fusion bonding layer,and the second portion of the fusion bonding layer being free of theTSV.
 9. The device of claim 1, wherein the capping substrate includes anintegrated circuit.
 10. A method of forming a micro-electro mechanicalsystem (MEMS) structure, the method comprising: providing a firstsubstrate structure having a first layer with a first silicon surface;providing a second substrate having a second layer with a second siliconsurface; bonding the second substrate structure to the first substratestructure using fusion bonding at a temperature between about 500Celsius and 1200 Celsius, wherein the fusion bonding fuses the firstlayer and the second layer by fusing the first and second siliconsurfaces to form a fusion bonding interface, wherein the secondsubstrate structure includes at least one micro-electro mechanicalsystem (MEMS) device, and wherein there is at least one cavitysurrounding at least a portion of the MEMS device; thinning the firstsubstrate to provide a first surface of the thinned first substrate; andforming a TSV in the first substrate structure and through the fusionbonding interface between the first substrate and the second substratesuch that a metal layer of the TSV extends through the fusion bondinginterface, wherein the forming the TSV includes forming an isolationlayer directly on the first surface of the thinned first substrate. 11.The method of claim 10, further comprising: forming an under bumpmetallurgy (UBM) layer over the first substrate structure, wherein theUBM layer contacts the metal layer used to fill the TSV.
 12. The methodof claim 10, wherein bonding the second substrate to the first substratecomprises forming a bonding ratio in a range from about 40% to about95%.
 13. The method of claim 10, further comprising, prior to the fusingthe first silicon surface and the second silicon surface, making thefirst and second silicon surfaces hydrophobic.
 14. A method of forming amicro-electro mechanical system (MEMS) structure, the method comprising:providing a first substrate structure having a first layer with a firstsilicon surface; providing a second substrate having at least onemicro-electro mechanical system (MEMS) device and having a second layerwith a second silicon surface; fusion bonding the second substratestructure to the first substrate structure, wherein the fusion bondingincludes: pressing together the first and second silicon surfaces;annealing the pressed together first and second silicon surfaces; andthereby forming a bonding interface between the first and second siliconsurfaces; and forming an interconnect through the first substrate andthe bonding interface to contact the second substrate.
 15. The method ofclaim 14, wherein the annealing is performed at between about 900Celsius and 1200 Celsius.
 16. The method of claim 14, wherein theforming the interconnect includes forming an opening in the firstsubstrate structure and the bonding interface; and depositing aconductive material in the opening to form a through silicon via (TSV).17. The method of claim 16, wherein the forming the interconnect furtherincludes doping a region of the second substrate, the doped region beingdisposed in the opening.
 18. The method of claim 17, wherein thedepositing the conductive material includes forming an interface betweenthe conductive material and the doped region.
 19. The method of claim14, further comprising: making the first silicon surface and the secondsilicon surface hydrophobic prior to the fusion bonding.
 20. The methodof claim 14, further comprising: thinning the first substrate after thefusion bonding and prior to forming the interconnect.